Variable amplitude fatigue crack growth characteristics of railroad tank car steel volume III
-
2006-12-01
Details:
-
Creators:
-
Corporate Creators:
-
Subject/TRT Terms:
-
Publication/ Report Number:
-
Resource Type:
-
TRIS Online Accession Number:01055619
-
Edition:Final report
-
Corporate Publisher:
-
NTL Classification:NTL-RAIL TRANSPORTATION-Rail Safety;NTL-RAIL TRANSPORTATION-RAIL TRANSPORTATION;
-
Abstract:The load history that railroad tank cars experience has a significant variable amplitude characteristic. Although previous efforts have been directed toward understanding baseline fatigue crack growth behavior of TC-128B steel as a function of material lot, orientation, and environment, little is known regarding how load interaction impacts crack growth behavior in a typical tank car steel. Load interaction occurs when the variable amplitude character of the loading results in crack growth that differs as a function of load history effects in the wake of the crack. The focus of this testing effort was to determine empirically how TC-128B behaves under these types of simplified loading conditions. The data provided in this report links the constant amplitude loading regime to the more complex variable amplitude-loading regime that tank cars experience during in-service use. The data can also be used as modeling guidelines to better understand the role of variable amplitude loading on TC-128B.
-
Format:
-
Funding:
-
Collection(s):
-
Main Document Checksum:
-
Download URL:
-
File Type:
Supporting Files
-
No Additional Files
More +